Quick Details
Place of Origin: China (Mainland) Model Number:6021/6020 Polyester Film
Product name: Polyester film Usage: for motor and transformer
Type: Insulation Film Material: Polyester film particle
Application: High Temperature, Cable, motor and transformer etc. Melting point: ≥256
Usage: Insulation Protection,electrical cable and wire, For backing material of Flexbile laminate and Motor& Transformer,slot insulation, interphase insulation and liner insulation
Relative dielectric constant (50Hz): 2.9~3.4 Processing Type: Multiple Extrusion
Tensile Strength: ≥120Mpa Width:325-3250mm or customized
Thickness: 12mic-500mic or Customers' requirements Core Size:3",6" or Customers' requirements
Roll Core ID:76mm(3") or 152mm(6" ), Core materials: Paper or plastic;
Feature: good dielectrical and high mechanical properties, Heat-Resistant
Weight of roll: 100kg-200kg or customized Color: 6020 transparent, 6021milky white
Style: roll, tape, sheet, strips Thermal class: E(120ºC)
Lead time: 10-15 days for one container Certification: ROHS and ISO9001
OEM, ODM service: Available Service: Die Cutting Slicing Slitting
Description
Polyester Film Composite Board is composed of layers polyester film which is coated with high temperature adhesive. It has good mechanical properties, electrical properties, shrinkage rate, water absorption and reliable heat resistance. It is mainly used for the insulation between the high and low voltage coils of the dry type transformer, which can be used as a substitute for the epoxy resin board and the phenolic resin board for the insulation tube and the end insulation.
6020&6021 is a biaxial oriented polythylene terephthalate(PET)film through melting, casting and stretching. This product has good dielectric and high mechanical properties. It is widely used for electrical insulation, such as slot insulation, interphase insulation and liner insulation in electric motors, and producing insulating flexible laminates.
Polyester Film for Electrical Insulation
6020-Polyester Film For Electrical Insulation (Transparent)
6021-Polyester Film For Electrical Insulation (Milky white)
6020/6021 Polyester film is biaxially oriented polyethylene terephthalate (PET) film.
6020 is a transparent film. 6021 is a milky white film.
It is Class E insulating material.
This product has good dielectrical and high mechanical properties.
Thermal class: E(120ºC)
Characteristics: flat, low shrinkage, excellent insulation properties, UL approved
Applications
Polyester Film is made from Polyethylene terephthalate by casting & Biaxially oriented.
It is widely used for the end wrap insulation, liner insulation of electrical oils, electromagnetic wire wrap insulation, cable wrapping on motor, transformer or other electrical appliances. It also be used for packaging, glass-steel, collar of clothes, etc.
It can be used as an electrical insulation and as a laminate with other substrates.
In motor applications, selected types of polyester film can be used for ground insulation as slot liners and wedges, as well as phase insulation. In wire and cable applications, it is ideal for mechanical barriers.
In addition, specialized polyester film can be used in transformer and high-voltage distribution equipment to wrap the conductors. They are effective for use in hermetic applications with refrigerator and air conditioner motor / compressor assemblies.
Roll or tapes White Mylar pet film,pet film tape, It is suitable for electrical insulation, such as slot insulation, Interphase insulation and liner insulation in electric motor, wrapping insulation for coils and cables, as well as producing insulating flexible composite material.
Advantages of PET
1. It has good mechanical properties and folding tolerance
2. It is resistant to oil, fat, dilute acid and alkali, most solvent.
3. It has excellent temperature tolerance. Long-term workable under 120°C ,
shortterm appliable under (150°Cor -70°C)slightly affection to its mechanical
properties under high or low temperature
4. It has low gas and vapor permeability, and good resistance to gas, water,
oil and odor.
5. It has high transparency and glossy, also can block ultraviolet ray.
6. It can be directly used in food packing since it is non-toxic, unscented with good sanitary security.
6020 Transparent PET Electrical Insulating Polyester Film Feature:
High transparency
Good brightness aluminum
Aluminum layer with good adhesion
Good products process ability
Excellent mechanical properties
High transparency
Bright color
High impact
No crystal points or waves on surface
Good performance in folding
Stable quality
High dimensional stability
Easy coating property
Excellent electrical insulation.
6021 Milky White mylar polyester film
6021 polyester film is biaxially oriented polyethelene terphthalate(PET)film
6021 is a mily white film
this product has good dielectrical and high mechanical properties.
Application:
It is suitable for electrical insulation,such as slot insulation,interphase insulation and liner insulation in electric motor transformer and other electric appliances ,wrapping insulation for coils and cables,as well as producing insulating flexible composit material.
Applications
• Electrical flexible laminates Electrical flexible laminates (DMD, MMM etc)
• Wire & cable Insulation, slot liner insulation, interlayer insulation in Motor, transformer etc.
• Adhesive tapes
•. Polyester label.
•. Polyester tubing.
•. Keyboard insulation
• TV/Monitor insulation
Mylar polyester film for electric motor insulation biaxially oriented polyethelene terephthalate (PET) film, which is a milky white film. It is Class E insulating material. This product has good dielectrical and high mechanical properties. It is suitable for electrical insulation, such as slot insulation, interphase insulation and liner insulation in electric motor, wrapping insulation for coils and cables, as well as producing insulating flexible composite material.
This type of film is used as an electrical insulation in motor applications, for ground insulation, as slot liner and wedges, phase insulation. it is ideal for mechanical barriers, as well as in transformer and high-voltage distribution equipment insulation separator and in addition its hardness is much suitable for automatic coil winding machines for fan industries and is also used in shirt collar bones for garments industry.
6021 Features
• Excellent electrical insulation.
• Thermal stability at elevated temperatures
• insulate class:E
• product description:
•Dimensional stability
• Coefficient of friction
•Tensile break strength
•Tensile yield strength
•Elongation at break
•Chemical and electrical resistance
•High dielectric constant
•Lower extractable content
•High electrical breakdown voltage
•High dimensional stability
•Easy coating property
Typical property
Three layer co-extrusion structure
High tensile strength and low heat shrinkage in high working temperature
High breakdown voltage and good electrical insulation
Stable quality
Technical parameter
| Properties |
Unit NO. |
1# |
2# |
3# |
4# |
5# |
6# |
7# |
8# |
Test method |
|
| Thickness |
μm |
36 |
50 |
75 |
100 |
125 |
150 |
188 |
250 |
GB12802.2 |
|
| Tensile Strength |
MD |
Mpa |
200 |
200 |
182 |
185 |
175 |
170 |
172 |
180 |
GB12802.2 |
|
| TD |
Mpa |
210 |
198 |
198 |
190 |
186 |
206 |
185 |
200 |
GB12802.2 |
|
| Elongation at break |
MD |
% |
115 |
125 |
115 |
120 |
150 |
130 |
150 |
148 |
GB12802.2 |
|
| TD |
% |
105 |
130 |
110 |
102 |
110 |
100 |
110 |
109 |
GB12802.2 |
|
| Shrinkage |
MD |
% |
1.3 |
1.4 |
1.3 |
1.3 |
1.4 |
1.4 |
1.5 |
1.8 |
GB12802.2 |
|
| (150ºC30min) |
TD |
% |
0.8 |
0.8 |
0.9 |
0.8 |
1.0 |
1.0 |
1.0 |
1.5 |
GB12802.2 |
|
| Breakdown voltage |
V/μm |
220 |
188 |
165 |
145 |
126 |
123 |
104 |
92 |
GB12802.2 |
|
| Volume resistivity |
Ω.m |
1.0×1014 |
1.0×1014 |
1.0×1014 |
1.0×1014 |
1.0×1014 |
1.0×1014 |
1.0×1014 |
1.0×1014 |
GB12802.2 |
|
| Ralative dielectric constant(48Hz-62Hz) |
|
3.0 |
3.0 |
3.0 |
3.0 |
3.0 |
3.0 |
3.0 |
3.0 |
GB12802.2 |
|
| |
| Dielectric loss tangent(48Hz-62Hz) |
|
2.8×10-3 |
2.8×10-3 |
2.8×10-3 |
2.8×10-3 |
2.8×10-3 |
2.8×10-3 |
2.8×10-3 |
2.8×10-3 |
GB12802.2 |
|
| |
| Haze |
% |
10.0 |
14.0 |
20.0 |
25.0 |
28.0 |
30.0 |
35.0 |
40.0 |
GB2410 |
|
| Light Transmittance |
% |
66 |
60 |
52 |
39 |
35 |
31 |
29 |
26 |
GB2410 |
|
| Gloss(45)° |
% |
98 |
90 |
84 |
80 |
76 |
76 |
74 |
70 |
GB8807 |
|
| Density |
g/cm3 |
1.4 |
1.4 |
1.4 |
1.4 |
1.4 |
1.4 |
1.4 |
1.4 |
GB12802.2 |
|
| Flame retardancy |
|
VTM-2 |
VTM-2 |
VTM-2 |
VTM-2 |
VTM-2 |
VTM-2 |
VTM-2 |
VTM-2 |
ANSI/UL94
|
|
| Properties |
Units |
Values |
| Tensile strength(MD and TD) |
25μm~100μm
>100μm~190μm
>190μm |
mpa |
≥150
≥140
≥110 |
| Elongation at break (MD and TD) |
25μm~50μm
>50μm~350μm |
% |
≥60
≥80 |
| Shrinkage (MD and TD) |
25~190μm
>190μm |
% |
≤3.0
≤2.0 |
| Volume resistivity |
Ω·M |
≥1.0×1014 |
| Relative dielectric constant (50Hz) |
|
2.9~3.4 |
| Dielectric dissipation factor (50Hz) |
|
≤5.0×10-3 |
| Density |
kg/m3 |
6020 |
6021 |
| 1390±10 |
1400+10-20 |
| Melting point |
ºC |
≥256 |
| Surface resistivity |
Ω |
≥1.0×1013 |
| Electrolytic corrosion |
Ocular estimate |
Class |
A1 |
| Metallic conductivity tensile Strength method |
% |
≤2 |
Dimensional stability
in high temp. |
With tension |
ºC |
≥200 |
| With pressure |
≥200 |
Technical indicators (aluminum substrate physical, mechanical performance):
| Performance |
Unit |
Test method |
Target |
| Tensile strength |
TD≥ |
MPa |
ASTM D-882 |
230 |
| MD≥ |
MPa |
230 |
| Elongation at break |
MD≥ |
% |
ASTM D-882 |
120 |
| TD≥ |
% |
120 |
| Modulus of elasticity |
MD≥ |
MPa |
ASTM D-882 |
4300 |
| TD≥ |
MPa |
4500 |
| Heat shrinkage rate |
MD≤ |
% |
ASTM D-1204 |
2 |
| 150ºC,30min |
TD≤ |
% |
0.5 |
| Coefficient of friction |
Static≤ |
|
ASTM D-1894 |
0.55 |
| Dynamic≤ |
|
0.45 |
| Haze |
General type≤ |
% |
ASTM D-1003 |
2 |
| Highlight type≤ |
% |
1.6 |
| Glossiness |
General type≥ |
% |
GB/T 8807 |
120 |
| Highlight type≥ |
% |
130 |
| Surface tension |
No treated≤ |
Dyne/cm |
ASTM D-2578 |
42 |
| Treated≥ |
Dyne/cm |
52 |
Note: special products can be customized according to customer specific requirements.
Main Specification
| Properties |
Thickness |
Unit |
Value |
Thickness
Tolerance |
12~100 mm
≥100 mm |
% |
≤±5
≤±4 |
| Tensile strength |
12~≤100 mm
>100~188 mm
≥188 mm |
MPa |
≥150
≥140
≥110 |
| Elongation at rupture |
12~23mm
25~<50 mm
≥50~350 mm |
% |
≥40
≥60
≥80 |
Heat
Shrinkage |
12~23mm
25~188 mm
≥188 mm |
% |
≤3.5
≤3.0
≤2.0 |
| Breakdown strength |
12mm
19mm
23mm
25 mm
36 mm
50 mm
75 mm
100 mm
125 mm
150 mm
188 mm
250 mm
300 mm
350mm |
V / mm |
≥208
≥190
≥174
≥170
≥150
≥130
≥105
≥ 90
≥ 75
≥ 70
≥ 65
≥ 60
≥ 55
≥ 50 |
Note: Above values are the accumulative typical ones by recognized testing method, but, in order to ensure you to select our products properly, please refer to above specification and test the samples based on your using purpose or feel free to contact us for more details.
FAQ
Q1: How about MOQ?
MOQ is according to different products. Whatever you need, we are glad to quote best price with good quality.
Q2: Can you send samples for testing?
500g Samples are free supplied, but express freight should be taken by client. After making order, we'd like to return freight back.
Q3: How can you guarantee the quality of mass goods is same as the sample sent to me before?
We kept another same sample and marked on company when we sent to customer. So our production will be based on.
Q4: Which package do you use?
Package is important part to avoid goods breaking in transportation. We will choose suitable packing depend on materials.
Q5: When customer respond quality issues after pick up goods, how to deal with?
1) Customer could supply photos of issued goods for our sales staff and then we'll verify which part is wrong.
2) If the issue is confirmed, company will negotiate with customers and compensate in coming orders.
Q6:What are your main products?
A:For oil immersed transformers, like Diamond dotted paper/DDP, Crepe paper tube, pressboard and so on.
For dry type transformers, like Class F DMD,NMN,AMA,NHN, and so on.
Packaging & Delivery
Packaging Details: each roll with protective film and carton, then with standard export pallets
Roll Core ID:76mm(3") or 152mm(6" ), Core materials: Paper or plastic;
Delivery Detail: 10-15 days for a container
Port: Shanghai, Qingdao, Shenzhen
Lead Time : Shipped in 15 days after payment
Please Contact Us
Miss: lydia
Mob: 86-13752439076 Fax: 86-22-60863016
http://chinainsulation.en.made-in-china.com
Audited Supplier 
){kind=link}